US20030205552A1 - Method of forming a membrane with nanometer scale pores and application to biofiltration - Google Patents
Method of forming a membrane with nanometer scale pores and application to biofiltration Download PDFInfo
- Publication number
- US20030205552A1 US20030205552A1 US10/439,892 US43989203A US2003205552A1 US 20030205552 A1 US20030205552 A1 US 20030205552A1 US 43989203 A US43989203 A US 43989203A US 2003205552 A1 US2003205552 A1 US 2003205552A1
- Authority
- US
- United States
- Prior art keywords
- layer
- base layer
- membrane
- etch stop
- forming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method of forming a membrane having nanometer scale pores includes forming an etch stop layer on a substrate and forming a base layer on the etch stop layer. Advantageously, a silicon nitride etch stop layer is formed on a silicon substrate and the base layer is a thermally grown oxide layer. Micron scale holes are etched through the base layer and, advantageously, partially through the underlying etch stop layer. A sacrificial base layer of controlled thickness is formed on the base layer and lining the holes. A thermally grown oxide is advantageously used as the sacrificial base layer. A plug layer is then formed on the base layer, on the sacrificial base layer and filling the holes. Polysilicon is advantageously used as the plug layer. The plug layer is planarized followed by the creation of an aperture in the backside of the wafer. Release of the etch stop layer and the sacrificial base layer results in a membrane having pores therein with lateral dimensions determined by the thickness of the sacrificial base layer, typically less than about 50 nm. Such membranes are shown to be favorably used in biofiltration and bioseparation applications.
Description
- This application is a continuation-in-part of U.S. patent application Ser. No. 09/715,840, filed Nov. 17, 2000 which derives from provisional patent application No. 60/166,049 filed Nov. 17, 1999, the entire disclosures of which are incorporated herein by reference.
- 1. Field of Invention
- This invention relates generally to the field of membranes having nanometer scale pores that can be used in biofiltration and bioseparation applications. More particularly, this invention relates to the formation of such membranes with microfabrication techniques.
- 2. Description of the Prior Art
- There is a revolution occurring in biological research with emphasis rapidly shifting towards the view of biology in terms of complex physical and chemical interactions. Interdisciplinary research between engineers, biologists, physicists, and clinicians is becoming prevalent. A rapidly developing field of research is the use of microfabrication to make mechanically, electrically, and/or chemically interactive structures for biological research and applications, known collectively as BIOMEMs (BIOlogical MicroElectroMechanical devices). By using microfabrication techniques derived from techniques developed to process semiconductors, MEMs structures can be fabricated with spatial features having typical dimensions ranging from the sub-micron range up to several millimeters. These multi-scale structures correspond well with hierarchical biological structures, from proteins and sub-cellular organelles to tissues and organs. This structural hierarchical correlation between biological structures and fabricated structures allows scientists to investigate biological structures on their respective size scales and interact in more appropriate and responsive manners to the structures within the body and within biological fluids.
- It would be desirable to use standard microlithography to produce structures that can be used for basic biological research, diagnostic, and therapeutic applications. However, conventional lithographic techniques have feature size limitations that prevent their use for fabricating structures that can physically interact with molecules of biological interest, such as proteins, nucleotides, and various physiological nutrients. To interact directly with these molecules, features must be fabricated with typical sizes less than approximately 50 nm (nm=nanometer=10−9 meter), which is not projected to be attainable by state of the art lithography until the year 2008. Furthermore, because of the fabrication techniques typically used for MEMS structures, and the potential for contamination they introduce, state of the art equipment will typically not be used to fabricate structures intended for biological applications, leading to a further delay in the fabrication of direct interaction structures.
- An example of structures having several uses in biological and other research fields is a membrane having nanometer scale (“nanoscale”) pores therein that would be useful for biofiltrations, separations, and other purposes. In particular, a uniform size distribution of pore openings without the presence of over-sized pores, would prevent even small amounts of undesirably large material from passing through the membrane.
- Previous techniques to fabricate membranes having nanoscale pores (or “nanopore membranes”) include the work of Chu et al (U.S. Pat. No. 5,770,076), the work done by the IBM Corporation (“Process for Producing a Precision Filter”, IBM Technical Disclosure Bulletin, Vol. 32, No. 4A, September 1989), among others. However, these approaches typically include one or more disadvantages. Typically, boron or other doping is used to produce etching selectivity among various elements of the structure that, when selectively etched, produce the nanoscale pores. However, boron doping can be subject to imprecise diffusion and, hence, imprecise geometric control of the membrane structure. Boron doping can also introduce undesirable mechanical stress into the membrane. Fabrication techniques described herein produce nanoscale pores without the necessity of doping with boron or any other dopant.
- Other membranes having nanoscale pores are fabricated having angled paths through the membrane, including right angle turns as in the filters of Chu et al (supra). While such pores can be useful for many practical applications, the introduction of turns and curves increases the likelihood of fouling or clogging by the filtered material. Thus, a direct path for the nanoscale pores through the membrane is desired, and such paths are produced by the techniques described herein.
- In view of the foregoing, a need exists in the art for a technique for fabricating membranes with features less than approximately 50 nm, without doping and including direct paths through the membrane. Ideally, such a technique would rely upon standard lithography processing techniques and would yield a device that is compatible with biological research, diagnostic, and therapeutic applications.
- Accordingly and advantageously, the invention provides a method of forming a membrane having nanometer scale pores therein. An etch stop layer is formed on a substrate and a base layer is then formed on the etch stop layer. Advantageously, pursuant to some embodiments of the invention, a silicon nitride etch stop layer is formed on a silicon substrate and the base layer is a thermally grown oxide layer. Micron scale holes are etched through the base layer and, advantageously, partially through the underlying etch stop layer. That is, holes are etched completely through the base layer and, perhaps into, but not completely through, the etch stop layer.
- A sacrificial base layer is formed on the base layer and lining the holes. Removal of the sacrificial base layer will form the nanometer scale pores. Thus, the thickness of the sacrificial base layer determines the lateral extent of the pores and should be accurately and carefully controlled for uniformity of pore size. A thermally grown oxide is advantageously used as the sacrificial base layer.
- A plug layer is then formed on the base layer, on the sacrificial base layer and filling the holes in those regions unoccupied by sacrificial base layer. Polysilicon is advantageously deposited as the plug layer.
- The plug layer is planarized (and optionally polished), followed by the creation of an aperture in the backside of the wafer. Protective layers are typically used on both sides of the wafer to protect the plug and sacrificial base layers during aperture formation, then removed. Release of the etch stop layer and the sacrificial base layers results in a membrane having pores therein with lateral dimensions determined by the thickness of the sacrificial base layer, typically less than about 50 nm. The pores fabricated in membranes pursuant to embodiments of the present invention traverse the membrane directly, without bends or right angle turns, thereby reducing the tendency to clog or foul during biofiltration or bioseparation.
- Unlike many prior art procedures for the fabrication of nanopore filters, the present techniques do not use doping (typically boron doping) of any layer to produce etching selectivity. Absence of doping typically results in better dimensional control and fewer mechanical stresses within the membrane.
- Membranes produced pursuant to embodiments of the present invention are capable of achieving a glucose diffusion test result of at least 1 mg/dl and an albumin diffusion test result of at most 0.1 g/dl. Further, the present membranes exhibit no significant biofouling or agglomeration of protein in the pores, in contrast to commercially available membranes.
- These and other advantages are achieved in accordance with the present invention as described in detail below.
- To facilitate understanding, identical reference numerals have been used, where possible, to designate identical elements that are common to the figures. The drawings are not to scale and the relative dimensions of various elements in the drawings are depicted schematically and not to scale.
- The techniques of the present invention can readily be understood by considering the following detailed description in conjunction with the accompanying drawings, in which:
- FIG. 1 depicts in cross sectional view a substrate with an etch stop layer formed thereon.
- FIG. 2 depicts in cross sectional view a base layer formed on the etch stop layer of FIG. 1.
- FIG. 3 depicts in cross sectional view micrometer scale holes etched through the base layer of FIG. 2 and partially through the etch stop layer.
- FIG. 4 depicts in cross sectional view the formation of a sacrificial base layer on the structure of FIG. 3.
- FIG. 5 depicts in cross sectional view anchor points formed in the sacrificial base layer of FIG. 4.
- FIG. 6 depicts in cross sectional view a plug layer formed on top of and filling the micrometer scale holes of FIG. 5.
- FIG. 7 depicts in cross sectional view the plug layer of FIG. 6 after planarization.
- FIG. 8A depicts in cross sectional view a protective layer formed on both sides of the wafer of FIG. 7.
- FIG. 8B depicts in cross sectional view the result of patterning and etching an aperture in the substrate of FIG. 8A.
- FIG. 9A depicts in cross sectional view the result of removing the protective layers from both sides of the wafer of FIG. 8B.
- FIG. 9B depicts in cross sectional view a membrane having nanometer scale pores therein following release of the exposed etch stop layer and sacrificial base layer of FIG. 9B.
- FIG. 10 summarizes typical processing steps used in fabrication of the structures depicted in FIGS.1-9B.
- FIG. 11 depicts in schematic, cut-away view a device used to test the membrane of the invention.
- FIG. 12 is a graphical comparison of glucose diffusion through three different nanopore membranes, WHATMAN (♦), MILLIPORE (bare line) and the micromachined nanopore membrane of the invention (▪)
- FIG. 13 is a graphical comparison of the diffusion of glucose and albumin through a typical nanopore membrane of the invention.
- FIG. 14 is a graphical comparison of glucose diffusion through a typical nanopore membrane of the invention incubated in pure glucose and mixed glucose/albumin solutions.
- FIG. 15 is a graphical comparison of diffusion through MILLIPORE membranes incubated in pure glucose and mixed glucose/albumin solutions
- FIG. 16 compares albumin diffusion through WHATMAN filters, MILLIPORE filters and a typical micromachined nanopore filter of the invention.
- After considering the following description, those skilled in the art will clearly realize that the teachings of the invention can be readily utilized in the fabrication of porous membranes having nanometer scale pores therein (also referred to herein as “micromachined” or “microfabricated” membranes), and the use of such membranes for filtration and separation. Typical procedures for fabrication of micromachined membranes pursuant to some embodiments of the present invention are illustrated in the accompanying figures.
- FIG. 1 depicts in cross sectional view (not to scale) a
typical substrate 20 having anetch stop layer 22 thereon. To be concrete in our description, we describe the detailed processing steps advantageously employed pursuant to some embodiments of the present invention for the fabrication of porous membranes deriving from silicon-based structures. However, the techniques described herein can also be employed in connection with the fabrication of porous membranes deriving from other materials. For biofiltration or separation, such other materials are advantageously selected to be biocompatible, such as metals (e.g., titanium), ceramics (e.g., silica, silicon nitride, polymers (e.g., polytetrafluoroethylene, polymethylmethacrylate, polystryenes, silicones), among others. -
Substrate 20 is typically a silicon wafer. Since theetch stop layer 22 is typically thin, it is advantageous in some embodiments to etch support ridges in the surface ofsubstrate 20 before depositing theetch stop layer 22 on top of the support ridges. When used, such support ridges (not depicted in FIG. 1) occur between thesubstrate 20 andetch stop layer 22. The support ridges help provide mechanical rigidity to the subsequently formed membrane structure. -
Etch stop layer 22 is employed in dual roles as an etch stop layer that is subsequently removed (or sacrificed) to expose the nanometer scale pores of the membrane. It thus functions as a sacrificial etch stop layer, buried beneath subsequent layers and may be precisely referred to as a “buried sacrificial etch stop layer.” However, for economy of language, we refer to layer 22 herein simply as an etch stop layer, understanding thereby that multiple functions are performed. - Advantageously, pursuant to some embodiments of the present invention,
etch stop layer 22 is low stress silicon nitride (“nitride”) typically deposited onsubstrate 20 by means of low pressure chemical vapor deposition. In some embodiments, the nitride etch stop layer has a thickness of approximately 0.4 μm [μm=micrometer (micron)=10−6 meter]. - Several advantages of the present invention derive from the multiple functions performed by
etch stop layer 22. For example, the buried, sacrificial nature of the etch stop layer facilitates three-dimensional control of the pore structure. Prior art techniques typically endeavor to control pore structure by balancing the etching of two different layers. The buried, sacrificial etch stop techniques employed in various embodiments of the present invention facilitate the formation of pores less than approximately 50 nm. Moreover, these pores can be uniformly formed across the entire wafer. - Techniques employed in various embodiments of the present invention achieve etching selectivity without the use of diffused boron, or other doping material. Diffused boron used as an etch stop typically results in an imprecise membrane depth due largely to the imprecise geometrical properties of diffusion during various processing steps occurring at elevated temperatures. Further, diffused boron introduces mechanical stresses into the completed membrane, advantageously avoided when boron diffusion is unnecessary.
- The buried, sacrificial etch stop layer employed in various embodiments of the present invention can also provide improved etching selectivity. That is, the etch stop layer is etched only negligibly by the KOH etchant typically employed. In contrast, boron-doped materials are typically etched to a rather greater extent by KOH etchant.
- Following deposition of the
etch stop layer 22, a base structural layer (“base layer”) 24 is deposited, as depicted in FIG. 2. In one embodiment, 5 μm of polysilicon is used as the base layer. In other embodiments, low stress silicon nitride may be used as the base layer, in which case it operates as its own etch stop layer. - Holes26 are then patterned and etched in
base layer 24 to define the shape of the pores in the final membrane (FIG. 3). The shape ofholes 26 can be determined by masking techniques known in the art. For example, theholes 26 may be etched through thepolysilicon base layer 24 by means of a chlorine plasma, with a thermally grown oxide layer used as a mask. Masking and production ofholes 26 follow techniques known in the art and, thus, these steps are not discussed in detail herein.Holes 26 typically have lateral dimensions of the order of μm, readily achievable with known techniques of microfabrication. - Holes26 should completely penetrate
base layer 24. Therefore, it is advantageous to employ a 10%-15% over-etch ofbase layer 24, as depicted in FIG. 3. Nitrideetch stop layer 22 typically acts as an etch stop layer for the plasma etching ofpolysilicon base layer 24 such that complete punch-through oflayer 22 is avoided. Complete punch-through is disadvantageous in thatmaterial filling holes 26 would not then be shielded from backside etching (typically with KOH etchant) applied from the substrate side of the membrane structure. Therefore, control of hole etching to avoid punch-through is desired. - A sacrificial base layer is grown on
base layer 24, and depicted as 28 in FIG. 4.Sacrificial base layer 28 is used to define the nanometer scale pores in the final membrane, so controlling the growth of this layer is an important factor in producing membranes with reproducible pore sizes. For polysilicon base layers, it is convenient to use a sacrificial silicon oxide layer for thesacrificial base layer 28. Typically, the sacrificial silicon oxide is grown by thermal oxidation of thebase layer 24, typically employing a growth temperature of between approximately 8500 to 9500 for approximately one hour with an annealing step of approximately ten minutes. - Other techniques can be used to form the
sacrificial base layer 28. For example, a thermally evaporated tungsten film can be used as a sacrificial base layer in connection with the fabrication of polymer membranes, and selectively removed with hydrogen peroxide. The primary characteristic of thesacrificial base layer 28 is the ability to control its thickness with high precision and high uniformity across the entire wafer, and hence across the entire membrane. A variable thickness occurring inlayer 28 typically leads to varying pore openings in the final membrane. Hence, a suboptimal membrane is the result, having at least some large pores capable of passing larger than desired materials. - Thermal oxidation of polysilicon and nitride layers allows the thickness of
sacrificial base layer 28 to be controlled to a precision of approximately 5% across the entire wafer. Limitations on this thickness control typically arise from local inhomogeneities in the base layer, such as variations of the initial thickness of the native oxide (especially for polysilicon), the grain size or density, and the impurity concentration. - A layer of material (“plug layer” or “plug material”) is to be deposited and fill
holes 26 in preparation for removal ofsacrificial base layer 28 and the formation of nanometer pores. However, it is advantageous in some embodiments of the present invention to provide for direct contact between the plug material and thebase layer 24 to help maintain pore spacing between layers, improve adhesion and mechanical strength, among other purposes. Thus, it is convenient to etch anchor points oranchor openings 30 insacrificial base layer 28. This is conveniently accomplished pursuant to some embodiments of the present invention by making use of the same mask used to defineholes 26 shifted diagonally by approximately 1 μm. This produces anchor points in one or two corners of each hole, thereby providing the desired mechanical connection between structural layers. - A
plug layer 32 is then deposited to fillholes 26 as well as coat the regions between holes, as depicted in FIG. 6. It is convenient to use approximately 1.5 μm of polysilicon for theplug layer 32 pursuant to some embodiments of the present invention.Plug layer 32 is then planarized to the level ofbase layer 24 as depicted in FIG. 7. - The method of planarization depends upon the material used as plug material. For realtively hard microfabrication materials (such as polysilicon and nitride), chemical mechanical planarization is a convenient method. Other materials could be planarized by means of a plasma etch, typically including a quick, wet chemical smoothing or polishing. Plasma etching has the potential advantage that it may be feasible to select a plasma and etching conditions such that the
base layer 24 is not affected. On the other hand, plasma etching has the potential disadvantage of the need for controlled etch timing to avoid deleterious etching of theplug material 32 residing inholes 26. - The portion of the membrane containing nanometer scale pores will derive from
structure 40 in FIG. 7. At this point, it is convenient to etch the lower (backside) portion ofsubstrate 20 to provide backside access to the membrane. To protect the upper (frontside) of the membrane during backside etch, it is convenient to apply a protective layer 34 to both the frontside of thewafer 34 f and the backside of thewafer 34 b, as depicted in FIG. 8. Protective layer 34 should be impervious or substantially undamaged by the etchant used to etch thesilicon substrate 20 such that, during etching ofsubstrate 20,protective layer 34 f on the frontside of the membrane protectsmembrane structure 40 from significant damage. For silicon etching by means of KOH with polysilicon and nitride layers it is found that a thin layer of nitride is conveniently used as protective layer 34, since nitride is insignificantly etched by KOH and only slowly dissolves in HF. For polymeric structural materials used to construct a membrane, silicone is conveniently used as a protective layer since the temperature of nitride deposition (typically around 835° C.) renders it impractical for use with polymers. - A backside etch window is patterned and etched in
protective layer 34 b, exposing thesilicon substrate 20 in desired areas.Silicon substrate 20 is then etched, typically by placing the entire structure in a KOH bath at a temperature of approximately 80° C. for sufficient time for thesilicon substrate 20 to etch up to the level of etch stop layer 22 (as evidenced by the smooth etch stop layer 22). FIG. 8B depicts theaperture 36 thereby created insubstrate 20. - Protective layer34 is now removed from both frontside and backside, resulting in the structure depicted in FIG. 9A. Thus, another characteristic desired of protective layer 34 is that it be removable without causing significant damage to the underlying membrane or other structures, resulting in a substantially undisturbed membrane as depicted in FIG. 9A.
- At this point, the portion of the
etch stop layer 22 exposed byaperture 36 and the remaining portions of thesacrificial base layer 28 are removed. For a nitrideetch stop layer 22 and an oxidesacrificial base layer 28, etching is advantageously performed by an HF or SF6/oxygen plasma. However, other etchants may also be employed and the removal of the etch stop layer and the sacrificial base layer can be done in distinct processing steps. In all such cases, the result is that eachhole 26 now contains one pore defined by the thickness ofsacrificial base layer 28. The pores thus having lateral dimensions in the range of nanometers are depicted by 41 in FIG. 9B. - FIG. 10 summarizes the foregoing processing steps: Form an etch stop layer on a substrate (step50). Form a base layer on the etch stop layer (step 52). Etch micrometer scale holes through the base layer and, advantageously, partially into the etch stop layer (step 54). Form a sacrificial base layer on the base layer and lining the micrometer scale holes (step 56). Pattern anchor points in the sacrificial base layer (step 58). Form a plug layer on the base layer and filling the micrometer scale holes (step 60) and planarize substantially to the level of the base layer (step 62). Protective layers are formed on both the frontside and backside of the wafer (step 64) followed by patterning and etching of the backside protective layer and underlying substrate to form an aperture (step 66). The protective layers are released or otherwise removed, advantageously accomplished in such manner as to cause no significant deleterious changes to other materials or structures (step 68). The etch stop layer is removed (in the region exposed by the aperture) and the sacrificial base layer is also removed from the micrometer scale holes, creating thereby nanometer scale pores (step 70).
- The performance of the
membrane 40 produced pursuant to some embodiments of the present invention was analyzed in comparison with two other types of membranes. In particular, a membrane 40 (with 24.5 nanometer pore size +/−0.9 nm) of the invention was compared with porous alumina (i.e., a WHATMAN ANODISC membrane with a pore size of 20 nm) and a mixed cellulose acetate and nitrate membrane (i.e., a MILLIPORE ISOPORE with a pore size of 25 nm). All membranes were examined in vitro by measuring relative concentrations of glucose on both sides of the microfabricated interface over time, using a mini diffusion chamber constructed around the membranes, as shown in FIG. 11. - FIG. 11 depicts a
chamber 80 with afirst compartment 82 and asecond compartment 84 with fixed volumes of approximately 2 ml.Sampling ports 86 are provided in each compartment. The compartments are at least partially separated by the membrane underconsideration 90. Advantageously, the two compartments are sealed with O-rings and are screwed together. - Glucose is measured on either side of the
membrane 90 in the diffusion chamber by means of a quantitative enzymatic assay (e.g., TRINDER, SIGMA) and calorimetric reading via a spectrophotometer. Samples of approximately 0.1 ml were taken from the diffusion chamber and approximately 10 μl of that sample were added to approximately 3 ml of glucose reagent in a cuvette, and were mixed gently by inversion. Each tube was incubated for approximately 18 minutes at room temperature and then readings were taken at a wavelength of 505 nm. The reagent is linear up to approximately 750 mg/dl. The diffusion chamber itself was attached to a motor for stirring in order to minimize boundary layer effects (diffusion resistance at the liquid/membrane interface). In order to ensure wetting of the pores, the receptor cell was first filled with phosphate buffer saline for about fifteen minutes before the filling of the donor cell. The donor cell was filled with solutions of glucose in phosphate buffer saline in varying concentrations. These tests were carried out at 37° C. - Albumin was measured on either side of the membrane using the same diffusion chamber. Albumin diffusion and/or exclusion was measured and quantified using Albumin BCP (bromocresol purple, SIGMA.) A sample of approximately 0.1 ml was taken at time zero and at the end of the diffusion period (time=330 minutes). An aliquot of approximately 300 μl was then added to approximately 3 ml of the reagent and absorbance was read at 600 nm. Reagent plus deionized water was used as the blank. The assay is linear up to approximately 6 g/dl but is not accurate below approximately 1 g/dl.
- FIGS.12-15 depict the results of these tests. The results demonstrate that glucose concentration increases and begins to plateau at about 330 minutes. FIG. 12 shows the diffusion of glucose from a pure glucose solution and a mixed solution of glucose and albumin through 24.5 nm pore-sized silicon membranes.
- The presence of albumin does not seem to impede passage of glucose through the membranes, nor slow down glucose transport under the experimental conditions employed. FIG. 13 shows that no detectable amounts of albumin diffuse through the microfabricated membrane. The same membrane, however, shows glucose diffusion. The microfabricated membranes are able to achieve complete exclusion of albumin (to within the limits of detection), while allowing glucose diffusion.
- Comparing these diffusion rates with those of commercially available membranes, it is seen in FIG. 14 that microfabricated filters pursuant to some embodiments of the invention have glucose diffusion properties comparable to the MILLIPORE and WHITMAN membranes with similar pore size. However, when albumin diffusion is measured for all three membranes, the nanopore micromachined membranes of the invention have the greatest albumin exclusion, as shown in the table of FIG. 16.
- The foregoing results illustrate glucose diffusion test results of at least 1 mg/dl in 330 minutes. The membrane has an albumin diffusion test result of at most 0.1 g/dl in 330 minutes.
- All of the membranes were evaluated before and after diffusion experiments to determine if any structural or surface changes had occurred. There were significant changes in membrane morphology for both the WHATMAN and MILLIPORE membranes after being incubated with glucose, albumin, and phosphate buffered saline for over 24 hours at 37° C. In contrast, the micromachined silicon membrane of the invention showed the same appearance before and after the tests. In fact, the microfabricated membrane pores are free from biofouling and any agglomeration of the protein in the pores. The MILLIPORE and WHATMAN membranes display inhomogeneities and morphological changes after all diffusion tests.
- In sum, the microfabricated silicon membranes of the invention were characterized in terms of glucose diffusion, albumin exclusion and stability in biological environments. Results indicated that glucose does indeed diffuse through the microfabricated membranes at a rate comparable to commercially available membranes. At the same time, albumin is excluded from passage. In a mixed solution of glucose and albumin, it has been shown that only glucose diffuses through the membranes. Although several membranes, such as those by WHATMAN and MILLIPORE are available for absolute filtration, these membranes do not have all the desired membrane properties, such as stability, bio-compatibility, and well-controlled perm-selectivity.
- The filter technology of the invention alleviates several of the problems associated with current commercially available separation membranes. Through the use of controlled sacrificial base layer deposition, membranes can be fabricated with sufficient precision to guarantee high pore uniformity in sub-micron dimensions. The thickness of the thermally grown oxide can be controlled to +/−1 nm for nominal pore sizes as small as approximately 18 nm. This is the size range needed to obtain absolute protein exclusion and glucose diffusion for biosensor applications. Moreover, this filter technology can bring in the added advantages of stability, minimal protein adsorption through established silicon surface modification techniques, reusability, and sterilizability.
- Although various embodiments which incorporate the teachings of the present invention have been shown and described in detail herein, those skilled in the art can readily devise many other varied embodiments that still incorporate these teachings.
Claims (14)
1. A method of forming a porous membrane comprising:
a) forming an etch stop layer on a substrate; and,
b) forming a base layer on said etch stop layer; and,
c) patterning and etching holes through said base layer and not completely through said etch stop layer; and,
d) forming a sacrificial base layer on said base layer and lining said holes, wherein said sacrificial base layer has a nanometer scale thickness, substantially uniform across the wafer; and,
e) forming a plug layer on said sacrificial base layer and filling said holes, wherein said plug layer is selectively removable in comparison with said sacrificial base layer without doping; and,
f) planarizing said plug layer; and,
g) patterning and etching an aperture through the backside of said substrate and through said etch stop layer, exposing thereby said plug layer and said sacrificial base layer; and,
h) selectively removing said sacrificial base layer, forming thereby nanometer scale pores through said base layer.
2. A method as in claim 1 further comprising the use of protective layers:
immediately following step f;
f1) forming protective layers on the frontside and backside of said wafer; and,
immediately following step g;
g1) removing remaining portions of said backside protective layer and said frontside protective layer; and.
3. A method as in claim 1 further comprising the use of support ridges:
immediately following step a;
a1) forming support ridges on said substrate.
4. A method as in claim 1 further comprising the use of anchor points:
immediately following step d;
d1) forming anchor points in said sacrificial base layer; and.
5. A method as in claim 1 wherein said substrate is a silicon wafer.
6. A method as in claim 5 wherein said etch stop layer is silicon nitride.
7. A method as in claim 6 wherein said sacrificial base layer is thermally formed oxide.
8. A method as in claim 7 wherein said plug layer is polysilicon.
9. A method as in claim 8 wherein said selective removal of said sacrificial base layer is with HF or SF6/oxygen plasma.
10. A method as in claim 1 wherein said nanometer scale pores are less than about 50 nanometers in lateral extent.
11. A biocompatible membrane produced according to the method of claim 1 having nanometer scale pores.
12. A membrane as in claim 11 wherein said membrane is derived from silicon compounds and has sub-fifty nanometer scale pores therein.
13. A membrane as in claim 12 wherein said membrane has a glucose diffusion test of at least 1 mg/dl and an albumin diffusion test of at most 0.1 g/dl over approximately 330 minutes.
14. A method of separating biological substances comprising filtering a mixture of said biological substances through a membrane as in claim 11 having nanometer scale pores therein.