CN104909558A - Method for preparing glassy state transparent quartz sand - Google Patents

Method for preparing glassy state transparent quartz sand Download PDF

Info

Publication number
CN104909558A
CN104909558A CN201510316770.1A CN201510316770A CN104909558A CN 104909558 A CN104909558 A CN 104909558A CN 201510316770 A CN201510316770 A CN 201510316770A CN 104909558 A CN104909558 A CN 104909558A
Authority
CN
China
Prior art keywords
quartz sand
transparent quartz
warming
glassy transparent
method preparing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510316770.1A
Other languages
Chinese (zh)
Other versions
CN104909558B (en
Inventor
周永恒
严颖
丁家兴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Hongwei quartz Technology Co., Ltd
Original Assignee
LIANYUNGANG HONGWEI QUARTS PRODUCT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIANYUNGANG HONGWEI QUARTS PRODUCT CO Ltd filed Critical LIANYUNGANG HONGWEI QUARTS PRODUCT CO Ltd
Priority to CN201510316770.1A priority Critical patent/CN104909558B/en
Publication of CN104909558A publication Critical patent/CN104909558A/en
Application granted granted Critical
Publication of CN104909558B publication Critical patent/CN104909558B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention provides a method for preparing glassy state transparent quartz sand. The method is characterized by comprising the following steps: placing synthesized high-purity silicon dioxide powder in a vacuum furnace, raising temperature to 1100-1500 DEG C, keeping temperature for 1-10 hours, and then raising temperature to 1700-1800 DEG C to keep temperature for 5-30 min, cooling to prepare a porous transparent quartz glass block, and crushing the block body to obtain the glassy state transparent quartz sand.

Description

A kind of method preparing glassy transparent quartz sand
Technical field
The invention belongs to quartz material preparation field, particularly prepare the method for glassy transparent quartz sand with synthesis high-purity silicon dioxide powder.
Background technology
One of silica glass is the special industrial glass of silicon-dioxide one-component, has the physical and chemical performance of multiple uniqueness, is space technology, nuclear industry, defence equipment, and material indispensable in the industry such as semi-conductor, electric light source, communication, light industry.
The raw material preparing silica glass has two large classes, comprises the natural matter such as crystal, quartz mine, and utilizes the Material synthesis such as silicon-containing compound such as silicon tetrachloride, water glass, silicon fluoride.Since earlier 1800s, the method that employing natural matter prepares silica glass is constantly perfect, and its output accounts for the 70-80% of whole quartz glass products.But due to the restriction of natural mineral raw crystalline structure, the bad problem of the quartz glass quality caused by the raw material containing impurity fails to be solved at all, make the silica glass prepared by natural matter cannot reach specification of quality needed for high-end technology industry.
Although adopt synthesis material to prepare silica glass can increase certain production cost, products obtained therefrom is applied to higher-end businesses, has more marketable value.China Patent Publication No. CN1541194A discloses a kind of preparation method of high purity synthetic vitreous silica particles, adopt synthesis material in nitrogen atmosphere, prepare highly purified silica glass particle, but its highest firing temperature is 1250 DEG C, the quartz products of this firing temperature gained is opaque, prepare transparency silica glass as raw material and need formulate sintering technology in addition, the product obtaining required transparency cannot be guaranteed.U.S. Patent Publication No. US6849242 discloses a kind of method of porous silica gel synthetic quartz glass powder, without fragmentation directly obtained fused silica powder, but this method need carry out hydrochlorination at 1100 to 1300 DEG C, finally burn till in the helium-atmosphere of 1500 DEG C, technological process is more complicated, and this sintering temperature is low, obtained product is opaque, cannot ensure the silica glass preparing required transparency as raw material equally.
Summary of the invention
The technical problem to be solved in the present invention designs a kind of method of technique simple and stable, prepares high-purity glassy transparent quartz sand.
Synthesis high-purity silicon dioxide powder of the present invention prepares the method for glassy transparent quartz sand, comprising: synthesis high-purity silicon dioxide powder is placed in vacuum oven, is warming up to 1100-1500 DEG C, insulation 1-10 hour; Be warming up to 1700-1800 DEG C of insulation 5-30 minute afterwards, after cooling, obtained porous transparency silica glass block, obtains glassy transparent quartz sand after fragmentation.
Further, the dioxide-containing silica in described synthesis high-purity silicon dioxide powder is greater than 99.99%.
Further, described vacuum oven gas pressure intensity is less than 1Pa.
Further, described vacuum oven gas pressure intensity is less than or equal to 1 × 10 -2pa.
Further, be warming up to 1100-1500 DEG C, described soaking time is 4-8 hour.
Further, described in be warming up to 1100-1500 DEG C, comprise and be warming up to 1100 DEG C soon, be then warming up to 1400-1500 DEG C slowly.
Further, described in be warming up to 1100-1500 DEG C, the speed comprising being not less than 20 DEG C/min is warming up to 1100 DEG C soon, is then warming up to 1400-1500 DEG C slowly with the speed being not more than 5 DEG C/min.
Further, described insulation 1-10 hour, afterwards to be not more than 5 DEG C/min ramp to 1700-1800 DEG C.
Compared with prior art, the invention has the advantages that: adopt aforesaid method technique simple and stable, synthesis high-purity silicon dioxide powder is utilized only to calcine in vacuum atmosphere, gained quartz glass block is after fragmentation, obtain the quartz sand of vitreous state, there is the characteristic of high-purity transparent, can be used as the raw material of the quartz glass products such as the inwall of monocrystalline silicon growing quartz crucible, photoconductive fiber.
Accompanying drawing explanation
Fig. 1 is the white quartz sand of comparative example 1 of the present invention;
Fig. 2 is the white quartz sand XRD test pattern shown in Fig. 1;
Fig. 3 is the white quartz sand XDR test pattern of comparative example 2 of the present invention;
Fig. 4 is the silica glass of embodiments of the invention 1;
Fig. 5 is the glassy transparent quartz sand obtained after the quartz glass block shown in Fig. 4 being ground;
Fig. 6 is the glassy transparent quartz sand XRD test pattern shown in Fig. 5.
Embodiment
Below in conjunction with the drawings and specific embodiments, the present invention is described in further detail.
The method preparing glassy transparent quartz sand of the present invention, synthesis high-purity silicon dioxide powder is placed in vacuum oven, and setting sintering procedure is: be warming up to 1100-1500 DEG C, insulation 1-10h; Be warming up to 1700-1800 DEG C, insulation 5-30min; Until taking out after quartz glass block cooling in stove, after fragmentation, obtain glassy transparent quartz sand.
Following examples further illustrate the present invention.
Comparative example 1:
High-purity silicon dioxide powder (dioxide-containing silica is greater than 99.99%) will be synthesized be placed in vacuum oven (gas pressure intensity is lower than 1 × 10 -2pa), setting sintering procedure is: fast heat up (speed is 20 DEG C/min), to 1200 DEG C, then slowly heat up (speed is 1 DEG C/min) is to 1450 DEG C of insulation 8h.Take out after making sample furnace cooling and obtain white quartz particles, after quartz particles is ground, obtain opaque white quartz sand (see Fig. 1).The XRD figure (see Fig. 2) of this white quartz sand shows that products obtained therefrom is cristobalite crystal formation.
Comparative example 2:
High-purity silicon dioxide powder (dioxide-containing silica is greater than 99.99%) will be synthesized be placed in vacuum oven (gas pressure intensity is lower than 1 × 10 -2pa), setting sintering procedure is: fast heat up (speed is 40 DEG C/min) is to 1100 DEG C, then be slowly warming up to 1450 DEG C (speed is 1 DEG C/min) and be incubated 4h, heat up slowly afterwards (speed is 5 DEG C/min) is to 1650 DEG C of insulation 10min.Take out after making sample furnace cooling and obtain white quartz particles, after quartz particles is ground, obtain quartz sand.The XRD figure (see Fig. 3) of this white quartz sand shows products obtained therefrom and contains vitreous silica and crystal state ashlar English two kinds of crystal formations.
Embodiment 1:
High-purity silicon dioxide powder (dioxide-containing silica is greater than 99.99%) will be synthesized be placed in vacuum oven (gas pressure intensity is lower than 1 × 10 -2pa), setting sintering procedure is: fast heat up (speed is 20 DEG C/min) is to 1100 DEG C, then be slowly warming up to 1450 DEG C (speed is 1 DEG C/min) and be incubated 4h, heat up slowly afterwards (speed is 5 DEG C/min) is to 1740 DEG C of insulation 10min.Take out after making sample furnace cooling and obtain porous transparency silica glass block (see Fig. 4), after quartz glass block is ground, obtain vitreous silica sand (see Fig. 5).
It has been vitreous state that the XRD figure (see Fig. 6) of this vitreous silica sand shows products obtained therefrom.
Embodiment 2:
High-purity silicon dioxide powder (dioxide-containing silica is greater than 99.99%) will be synthesized be placed in vacuum oven (gas pressure intensity is lower than 1 × 10 -2pa), setting sintering procedure is: fast heat up (speed is 30 DEG C/min) is to 1100 DEG C, then be slowly warming up to 1450 DEG C (speed is 3 DEG C/min) and be incubated 6h, heat up slowly afterwards (speed is 3 DEG C/min) is to 1760 DEG C of insulation 20min.Take out after making sample furnace cooling and obtain porous transparency silica glass block, after quartz glass block is ground, obtain vitreous silica sand.
The XRD figure display products obtained therefrom of this vitreous silica sand has been vitreous state.
Embodiment 3:
High-purity silicon dioxide powder (dioxide-containing silica is greater than 99.99%) will be synthesized be placed in vacuum oven (gas pressure intensity is lower than 1 × 10 -2pa), setting sintering procedure is: fast heat up (speed is 40 DEG C/min) is to 1100 DEG C, then be slowly warming up to 1450 DEG C (speed is 1 DEG C/min) and be incubated 8h, heat up slowly afterwards (speed is 1 DEG C/min) is to 1780 DEG C of insulation 30min.Take out after making sample furnace cooling and obtain porous transparency silica glass block, after quartz glass block is ground, obtain vitreous silica sand.
The XRD figure display products obtained therefrom of this vitreous silica sand has been vitreous state.
Comparative result table under table one, different condition
Condition Corresponding form
Comparative example 1 The white quartz sand of cristobalite crystal formation
Comparative example 2 White quartz sand containing vitreous silica and crystal state ashlar English two kinds of crystal formations
Embodiment 1 Glassy transparent quartz sand
Embodiment 2 Glassy transparent quartz sand
Embodiment 3 Glassy transparent quartz sand

Claims (9)

1. prepare a method for glassy transparent quartz sand, it is characterized in that: synthesis high-purity silicon dioxide powder is placed in vacuum oven, is warming up to 1100-1500 DEG C, insulation 1-10 hour; Be warming up to 1700-1800 DEG C of insulation 5-30 minute afterwards, after cooling, obtained porous transparency silica glass block, obtains glassy transparent quartz sand after fragmentation.
2. the method preparing glassy transparent quartz sand according to claim 1, is characterized in that: the dioxide-containing silica in described synthesis high-purity silicon dioxide powder is greater than 99.99%.
3. the method preparing glassy transparent quartz sand according to claim 1, is characterized in that: described vacuum oven gas pressure intensity is less than 1Pa.
4. the method preparing glassy transparent quartz sand according to claim 3, is characterized in that: described vacuum oven gas pressure intensity is less than or equal to 1 × 10 -2pa.
5. the method preparing glassy transparent quartz sand according to claim 1, is characterized in that: be warming up to 1100-1500 DEG C, and described soaking time is 4-8 hour.
6. the method preparing glassy transparent quartz sand according to claim 1, is characterized in that: described in be warming up to 1100-1500 DEG C, comprise and be warming up to 1100 DEG C soon, be then warming up to 1400-1500 DEG C slowly.
7. the method preparing glassy transparent quartz sand according to claim 6, it is characterized in that: described in be warming up to 1100-1500 DEG C, the speed comprising being not less than 20 DEG C/min is warming up to 1100 DEG C soon, is then warming up to 1400-1500 DEG C slowly with the speed being not more than 5 DEG C/min.
8. the method preparing glassy transparent quartz sand according to claim 1, is characterized in that: described insulation 1-10 hour, afterwards to be not more than 5 DEG C/min ramp to 1700-1800 DEG C.
9. product prepared by the method preparing glassy transparent quartz sand according to claim 1-8.
CN201510316770.1A 2015-06-10 2015-06-10 A kind of method for preparing glassy transparent quartz sand Active CN104909558B (en)